Printing Instructions |
|
Mitsubishi
|
®Hostaphan
KN
|
Polyethylene Terephthalate (PET)
|
|
|
|
|
|
Description
|
Hostaphan KN is made of high grade PET and characterised
by outstanding physical properties
|
Applications
|
Used as a number of important functions as a 'bundling'
film in cable and wire manufacture
|
Approvals
|
None
|
|
|
|
|
|
|
|
Properties |
Unit |
Test
Method |
Other |
|
|
|
Thickness
Micron |
um |
Micrometer
method
|
- |
12 |
50 |
125 |
Thickness Gauge |
gauge |
- |
- |
48 |
200 |
500 |
Thickness
Thous |
" |
- |
- |
.0005 |
.002 |
.005
|
Yield |
Substance Yield G/M2 |
G/M2 |
- |
- |
17 |
71 |
175 |
Yield
M2/ Kg |
M2/Kg |
|
|
59 |
14 |
5.7 |
Mechanical
Properties MD |
Tensile Strength |
N/mm2 |
ISO 527-1-2
|
test
speed100% 23degC,50%r.h. |
MD230 |
MD180
|
MD170 |
Elongation
at break |
% |
ISO 527-1-2
|
test
speed100% 23degC,50%r.h. |
MD90 |
MD160
|
MD170 |
Youngs
Modulus
|
N/mm2
|
ISO 527-1-2
|
test
speed100% 23degC,50%r.h.
|
MD4400
|
MD4000
|
MD3800
|
Tensile stress
|
N/mm2
|
ISO 527-1-2
|
test
speed100% 23degC,50%r.h.
|
MD110
|
MD110
|
MD110
|
Mechanical
Properties TD |
Tensile
Strength |
N/mm2 |
ISO 527-1-2
|
test
speed100% 23degC,50%r.h. |
TD260 |
TD280
|
TD260 |
Elongation
at break |
% |
ISO 527-1-2
|
test
speed100% 23degC,50%r.h. |
TD90 |
TD80
|
TD80 |
Youngs
Modulus
|
N/mm2
|
ISO 527-1-2
|
test
speed100% 23degC,50%r.h.
|
TD5200
|
TD5500
|
TD5300
|
Tensile stress
|
N/mm2
|
ISO 527-1-2
|
test
speed100% 23degC,50%r.h.
|
TD110
|
TD110
|
TD115
|
Thermal
MD |
Shrinkage |
% |
DIN 40634 or VDE 0345
|
150
degC, 15min |
MD 1.3 |
MD 1.0
|
MD 1.0 |
Thermal
TD |
Shrinkage |
% |
DIN 40634 or VDE 0345 |
150
degC, 15min |
TD 0.1 |
TD 0.3
|
TD 0.3 |
Low Tep resistance
|
deg C
|
-
|
-196
|
-
|
-
|
-
|
Thermal Conducivity
|
W/mxK
|
VDE 0304/part 1
|
0.13
|
-
|
-
|
-
|
Melting Point
|
deg C
|
Differential thermoanalysis
|
260
|
-
|
-
|
-
|
Physical/Chemical |
Density
|
g/cm2
|
ASTM-D 1505-68 Method C
|
1.395 23degC
|
-
|
-
|
-
|
Electrical
|
Dielectric constant
|
-
|
DIN 40634 or VDE 0345 in air
|
Value 3.3 23degC, 50Hz
|
-
|
-
|
-
|
Dielectric strength
|
kV/mm
|
DIN 40634 or VDE 0345 in air
|
Value
510, 380 12µ Value 460 240 50µ Value 420, 160, 125µ
|
DC/ AC, 50hZ
|
DC/ AC, 50hZ
|
DC/ AC, 50hZ
|
Dissipation factor
|
-
|
DIN 40634 or VDE 0345
|
Value 0.0020 23degC Hz
|
-
|
-
|
-
|
Volume resistivity
|
ohms x cm
|
DIN 40634 or VDE 0345
|
23degC,DC
|
10 to power 18
|
-
|
10 to power 17
|
|
|
Other
Specifications: Delivery Programme of Hostaphan KN in nominal
thicknesses of 12, 15, 19, 23, 36, 50, 75, 100 & 125 microns ® |
Hostaphan KN is water impermeable
and corrosion resistant and is a safe/reliable electrical insulation. |
Hostaphan MP is recommended as
a separating layer between the insulator itself and the individual
copper strands of the cable. |
|
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
®Hostaphan
is the registered trademark for Mitsubishi Polyester Film GmbH. |
|