ACRYLIC COATED POLYPROPYLENE FILM
|
|
 |
| |
| |
|
Description
|
Polymex® OP1A2 is a bioriented polypropylene film coated
on both sides with acrylic water based emulsion.
Main properties:
Excellent optical properties.
Outstanding machineability on the high speed automatic packaging
machines.
Excellent printability.
Good aroma barrier.
High stiffness.
Polymex® OP1A2 , as a result of a wide sealing range
and high seal strength, is suitable for all main packaging
applications.
Polymex® OP1A2, printable with the standard system
used for acrylic-coated film, is a reliable solution for
the most difficult packaging problems.
Polymex® OP1A2 enhances the presentation of the final
product.
|
Applications
|
Packaging
|
Pre-treatment
|
Both sides treated
|
Approvals
|
None
|
| |
|
|
|
 |
Properties |
Unit |
Typical
Value |
Test
Method |
|
|
|
Tensile Strength |
N/mm2 |
|
ASTM
D 882 |
|
|
|
MD |
|
120
|
DIN 53455 |
|
|
|
TD |
|
300
|
|
|
|
|
Elongation at break |
% |
|
ASTM
D 882 |
|
|
|
MD
|
|
210 |
DIN 53455 |
|
|
|
TD
|
|
50 |
|
|
|
|
Coefficient of friction film/film |
|
0.35 |
ASTM D 1894
|
|
|
|
Acr/Acr
(dynamic) |
|
|
DIN 53375 |
|
|
|
WVTR
|
g/m2 24h
|
5.5
|
ASTM F
1249
|
|
|
|
Thickness 25um
|
|
|
38°C-90%R.H
|
|
|
|
WVTR
|
g/m2 24h |
1.0
|
DIN 53122
|
|
|
|
Thickness 25um
|
|
|
23°C-85%R.H |
|
|
|
OTR
|
cm3/m2 24h atm
|
800
|
ASTM
D 1434
|
|
|
|
Thickness 25um
|
|
|
25°C-0%R.H |
|
|
|
Haze
|
% |
1.3
|
ASTM
D 1003 |
|
|
|
Thickness 25um |
- |
- |
- |
|
|
|
Gloss
|
% |
90 |
ASTM D 2457 |
|
|
|
Heat seal range |
°C |
100° ÷145°
|
Moplefan
A 29 |
|
|
|
|
Seal strength
|
N/cm |
2.0 |
OPMA TC4 (b) |
|
|
|
Thickness 25um |
- |
- |
|
|
|
|
|
Treatment Level
|
dyne/cm |
>38 |
ASTM D 2528 |
|
|
|
Polymex
OP1A2
|
Thickness |
20um |
25um |
30um |
35um |
40um |
|
g/m2 |
18.2 |
22.7 |
27.3 |
31.8 |
36.4
|
|
m2/kg |
54.9 |
44.1 |
36.6 |
31.4 |
27.5
|
|
|
|
Other
Specifications: |
|
|
|
PSG
Group Ltd. - Disclaimer
All technical information and related data supplied by or on behalf
of PSG
Group Ltd. (and subsidiary companies) is believed to be accurate
and
complete. However, it will remain the responsibility of the purchaser
/ user
to determine the suitability of each product for a particular application
and shall assume all risk and liability in connection therewith.
No warranty is implied with regard to information or recommendations
given
by our distributors and or subcontractors.
The descriptions of products and services displayed on this web site
and the
terms under which they are given may be modified at any time without
notice.
In any event or occurrence, our liability is strictly limited to
the value
of the original invoice.
Any links on this site are for the convenience of the visitor only
and we
are not responsible for their content. |
Polymex® is the registered
trademark of PSG Group |
|